KG-75-1
Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: technology
scope of application: for continuous steel teeming
KG-80
Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: technology
scope of application: for continuous steel teeming
KGBP-85
Type: aluminous
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming ladle slide gates
KSM
Type: siliciferous
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for service in various heat aggregates at high temperature load
KSSS
Type: siliciferous
Group: made of quartz (siliciferous) glass (SiO2 ≥ 98%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for free-flow output from tundish ladle into crystallizer pan