SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Heat treatment method
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 5
products found: 5
CRK
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
CRR-2
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
PHGT
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for steel teeming from ladle
SHPD-39
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of shank shoulders, shank shoulders, belly and cooled part of the blast furnaces with the volume not less than 1719m3, not cooled part of the shaft and blast-furnace mouths
SHPD-41
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of iron receiver of all the blast furnaces, shank shoulders, belly and cooled part of the blast furnace shaft with the volume 1719m3 and more