PATCHING BRIQUETTES BP
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
PHSST
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for melting space arch of open-hearth furnaces, operating without bath oxygen lancing, as well as arches of slag chambers and regenerators
БП-75
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-82
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-85
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining