DL-1.0
Type: siliciferous
Group: silica with additions (SiO2 - 80-93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
DL-1.2
Type: siliciferous
Group: silica with additions (SiO2 - 80-93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
MLL-1.3
Type: aluminosilicate
Group: mullite (Al2O3 62-72%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
P-89
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of high temperature furnaces
P-91
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of high temperature furnaces