SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Porosity degree
Heat treatment method
Molding process
Intended purpose
scope of application
Reference document for product properties
Filter result:
products found: 5
products found: 5
KST
Type: siliciferous
Group: made of quartz (siliciferous) glass (SiO2 ≥ 98%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for metal jet protection from oxidation
PATCHING BRIQUETTES BP
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-75
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-82
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-85
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining