SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Porosity degree
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 8
products found: 8
CRK
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
CRR-1
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
CRR-2
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
HP1
Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates
HP2
Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates