CRK
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
CRR-1
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
CRR-2
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
SHVG-30
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: lining of other areas (i.e., all, except lining of iron receiver, melting belt, tuyere area)
SHVG-33
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: lining of iron receiver, melting belt, tuyere area