SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Heat treatment method
scope of application
Reference document for product properties
Filter result:
products found: 6
products found: 6
CRS-1
Type: zirconium
Group: zircon
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of feed refractories (openings, plungers, etc.) open-hearth glass furnace
CRS-2
Type: zirconium
Group: zircon
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: elements of bottom plate and separation plate between Bacor and silica
KCI
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
MCI-1
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of burners, muffler, applied in flame area of open-hearth glass furnace
MCI-2
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction