SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Molding process
Intended purpose
scope of application
Reference document for product properties
Filter result:
products found: 6
products found: 6
CRK
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
CRR-1
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
CRR-2
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
KSM
Type: siliciferous
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for service in various heat aggregates at high temperature load
KSSS
Type: siliciferous
Group: made of quartz (siliciferous) glass (SiO2 ≥ 98%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for free-flow output from tundish ladle into crystallizer pan