SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Porosity degree
Heat treatment method
Molding process
Binding type 2
scope of application
Reference document for product properties
Filter result:
products found: 5
products found: 5
BMKP-80
Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: heat treated
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel blowing with inert gas
BMKRP-50
Type: aluminosilicate
Group: mullite silica (Al2O3 45-62%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: heat treated
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel blowing with inert gas
KSM
Type: siliciferous
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for service in various heat aggregates at high temperature load
KSSS
Type: siliciferous
Group: made of quartz (siliciferous) glass (SiO2 ≥ 98%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for free-flow output from tundish ladle into crystallizer pan
KST
Type: siliciferous
Group: made of quartz (siliciferous) glass (SiO2 ≥ 98%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for metal jet protection from oxidation