products found: 9
products found: 9
PGRBS-90
Type: oxicarbonous
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming ladle slide gates
PHSST
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for melting space arch of open-hearth furnaces, operating without bath oxygen lancing, as well as arches of slag chambers and regenerators
PLKU-94
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for lining of tap-holes for steel discharge from converter
PUBR-90
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming ladle slide gates