PBSP-88 (INSERT)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle
PBSP-88 (NOZZLE)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle
PHGT
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for steel teeming from ladle
SHGSP
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: soft mud forming
Intended purpose: technology
scope of application: for steel teeming from ladle
SHKL-1.3
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)