SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Heat treatment method
Molding process
Binding type 2
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 10
products found: 10
BMKP-80
Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: heat treated
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel blowing with inert gas
BMKRP-50
Type: aluminosilicate
Group: mullite silica (Al2O3 45-62%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: heat treated
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel blowing with inert gas
PBSP-88 (INSERT)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle
PBSP-88 (NOZZLE)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle
SHGSP
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: soft mud forming
Intended purpose: technology
scope of application: for steel teeming from ladle