SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Heat treatment method
Molding process
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 11
products found: 11
CRK
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
CRR-1
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
CRR-2
Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
PBSP-88 (INSERT)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle
PBSP-88 (NOZZLE)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle