Filter result:
products found: 5
products found: 5
KCI
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
KDBS-85
Type: aluminous
Group: alumina
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel teeming ladle slide gates
KF
Group: alumina
Refractoriness value: fire resistance (1580 to 1770°С)
scope of application: for protection of furnaces with temperature 1750°С from aggressive impact of melted metal, arch laying.
MCI-1
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of burners, muffler, applied in flame area of open-hearth glass furnace
MCI-2
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction