SELECT id, txt, site.txt_lang(txt, 3) as mark FROM products_marks WHERE type = 1 AND id IN (SELECT pm.id FROM products_marks pm, mark_properties mp WHERE pm.id = mp.mark AND property = 5 AND value IN (5) AND pm.id IN (SELECT pm.id FROM products_marks pm, mark_properties mp WHERE pm.id = mp.mark AND property = 10 AND value IN (38))) AND hidden IS false ORDER BY mark LIMIT 5 OFFSET 0

CRA

Type: zirconium
Group: zircon
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for continuous steel teeming

CRR-1

Type: zirconium
Group: oxide zirconium
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology

GIR-KS-1

Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for laying of various heat aggregates

GIR-KS-2

Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology

GIR-KS-3

Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology