DV
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot-blast stoves, hot blast mains, orifices and blast furnace tuyere connections
DVNK
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot-blast stoves, hot blast mains, orifices and blast furnace tuyere connections
KST
Type: siliciferous
Group: made of quartz (siliciferous) glass (SiO2 ≥ 98%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for metal jet protection from oxidation
PATCHING BRIQUETTES BP
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-75
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining