PATCHING BRIQUETTES BP
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
SHK-35
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of charging holes, inspection shafts, wall of coke and coke-pitch furnace regenerators, arch brick, gas burners
БП-75
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-82
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
БП-85
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining