DK-1
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
DK-1
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
DK-1
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
PBSP-88 (INSERT)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle
PBSP-88 (NOZZLE)
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming from ladle