SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Porosity degree
Heat treatment method
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 10
products found: 10
DV
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot-blast stoves, hot blast mains, orifices and blast furnace tuyere connections
KVKB
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles
MKRK-50
Type: aluminosilicate
Group: mullite silica (Al2O3 45-62%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in ladle working lining
MKV-72
Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot blast mains, orifices and blast furnace tuyere connections
SHKU-32
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: lining of steel teeming ladles