SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Porosity degree
Heat treatment method
Molding process
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 5
products found: 5
DL-1.0
Type: siliciferous
Group: silica with additions (SiO2 - 80-93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
DL-1.2
Type: siliciferous
Group: silica with additions (SiO2 - 80-93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
KSM
Type: siliciferous
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for service in various heat aggregates at high temperature load
MLL-1.3
Type: aluminosilicate
Group: mullite (Al2O3 62-72%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
PHKUTT
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for slag belt lining of steel teeming furnaces