SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Molding process
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 7
products found: 7
KSM
Type: siliciferous
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: casted
Intended purpose: technology
scope of application: for service in various heat aggregates at high temperature load
MCI-1
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of burners, muffler, applied in flame area of open-hearth glass furnace
SHKU-32
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: lining of steel teeming ladles
SHKU-37
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: lining of steel teeming ladles
SHKU-39
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: lining of steel teeming ladles