SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Heat treatment method
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 12
products found: 12
KVKB
Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles
MCI-1
Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of burners, muffler, applied in flame area of open-hearth glass furnace
PU-1
Type: oxicarbonous
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles
PU-10
Type: oxicarbonous
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles
PU-2
Type: oxicarbonous
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles