SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Heat treatment method
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 7
products found: 7
CRS-1
Type: zirconium
Group: zircon
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of feed refractories (openings, plungers, etc.) open-hearth glass furnace
PATCHING BRIQUETTES BP
Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining
SHVG-33
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: lining of iron receiver, melting belt, tuyere area
SHVG-35
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: lining of iron receiver, melting belt, tuyere area
БП-75
Type: high-magnesia
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for repair of converter working lining