products found: 6
SELECT id, txt, site.txt_lang(txt, 3) as mark FROM products_marks WHERE type = 1 AND id IN (SELECT pm.id FROM products_marks pm, mark_properties mp WHERE pm.id = mp.mark AND property = 12 AND value IN (11)) AND hidden IS false ORDER BY mark LIMIT 5 OFFSET 0

DV

Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot-blast stoves, hot blast mains, orifices and blast furnace tuyere connections

DVNK

Type: siliciferous
Group: silica (SiO2 > 93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot-blast stoves, hot blast mains, orifices and blast furnace tuyere connections

MKV-72

Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot blast mains, orifices and blast furnace tuyere connections

SHV-28

Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot blast mains, orifices and blast furnace tuyere connections

SHV-37

Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products for laying of hot blast mains, orifices and blast furnace tuyere connections