SHGSP
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: soft mud forming
Intended purpose: technology
scope of application: for steel teeming from ladle
SHPD-39
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of shank shoulders, shank shoulders, belly and cooled part of the blast furnaces with the volume not less than 1719m3, not cooled part of the shaft and blast-furnace mouths
SHPD-41
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of iron receiver of all the blast furnaces, shank shoulders, belly and cooled part of the blast furnace shaft with the volume 1719m3 and more
SHSP-32 (NOZZLE)
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: soft mud forming
Intended purpose: technology
scope of application: for steel teeming from ladle
SHSP-32 (PLUG)
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: soft mud forming
Intended purpose: technology
scope of application: for steel teeming from ladle