products found: 9
products found: 9
GIR-KS-4
Type: aluminosilicate
Group: mullite (Al2O3 62-72%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for laying of various heat aggregates
GIR-MLA-62
Type: aluminosilicate
Group: mullite (Al2O3 62-72%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of various heat aggregates
GIR-MLA-65
Type: aluminosilicate
Group: mullite (Al2O3 62-72%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of various heat aggregates
KDBS-85
Type: aluminous
Group: alumina
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel teeming ladle slide gates
KF
Group: alumina
Refractoriness value: fire resistance (1580 to 1770°С)
scope of application: for protection of furnaces with temperature 1750°С from aggressive impact of melted metal, arch laying.