SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Heat treatment method
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 11
products found: 11
DL-1.0
Type: siliciferous
Group: silica with additions (SiO2 - 80-93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
DL-1.2
Type: siliciferous
Group: silica with additions (SiO2 - 80-93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: highly-porous (Ptot 45-75%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: in working (not protected) lining of furnaces, not subject to exposure to melted iron, abrasion force and mechanical shocks, or in intermediate (protected insulation)
EDTSH
Type: siliciferous
Group: silica with additions (SiO2 - 80-93%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for electric-steelmaking furnaces
PHC
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of revolving furnaces, used in cement sector and other industry sectors
PHGB
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of arches of open-hearth, tandem and electric-steelmaking furnaces