• GIR - home
  • Selection of products according to the parameters

SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS

Type
Group
Refractoriness value
Porosity degree
Heat treatment method
Molding process
Binding type 1
Binding type 2
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 63
SELECT id, txt, site.txt_lang(txt, 3) as mark FROM products_marks WHERE type = 1 AND id IN (SELECT pm.id FROM products_marks pm, mark_properties mp WHERE pm.id = mp.mark AND property = 4 AND value IN (4)) AND hidden IS false ORDER BY mark LIMIT 5 OFFSET 15

HP3

Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates

HP4

Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates

HP5

Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates

KCI

Type: zirconium
Group: alumina-oxide zirconium-silicious
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction

KDBS-85

Type: aluminous
Group: alumina
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel teeming ladle slide gates