HP1
Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates
HP2
Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates
HP3
Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates
HP4
Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates
HP5
Type: magnesia spinel
Group: chrome-periclase (MgO 40-60%, Cr2O3 15-35%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of high temperature heat aggregates