SELECT id, txt, site.txt_lang(txt, 3) as mark FROM products_marks WHERE type = 1 AND id IN (SELECT pm.id FROM products_marks pm, mark_properties mp WHERE pm.id = mp.mark AND property = 8 AND value IN (7) AND pm.id IN (SELECT pm.id FROM products_marks pm, mark_properties mp WHERE pm.id = mp.mark AND property = 5 AND value IN (63))) AND hidden IS false ORDER BY mark LIMIT 5 OFFSET 0

BMKP-80

Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: heat treated
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel blowing with inert gas

BMKRP-50

Type: aluminosilicate
Group: mullite silica (Al2O3 45-62%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: heat treated
Molding process: vibrocasted, including concrete
Intended purpose: technology
scope of application: for steel blowing with inert gas

PHGT

Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: dense (Ptot 10-16%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for steel teeming from ladle

PHKUTT

Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for slag belt lining of steel teeming furnaces

PPT-95

Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming ladle slide gates