MKS-72
Type: aluminosilicate
Group: mullite-corundum (Al2O3 72-95%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of various heat aggregates
MLS-62
Type: aluminosilicate
Group: mullite (Al2O3 62-72%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of various heat aggregates
PHGB
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of arches of open-hearth, tandem and electric-steelmaking furnaces
PHSS
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for laying of arches of open-hearth furnaces
PHSST
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: high fire resistance (1770 to 2000°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for melting space arch of open-hearth furnaces, operating without bath oxygen lancing, as well as arches of slag chambers and regenerators