SELECTION OF PRODUCTS ACCORDING TO THE PARAMETERS
Type
Group
Refractoriness value
Porosity degree
Heat treatment method
Intended purpose
scope of application
Reference document for product properties
Reference documents for product dimensions
Filter result:
products found: 6
products found: 6
KP
Group: acid-resistant ware
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for protection of apparatuses and construction structures, operated under conditions of aggressive acid environment and at lining of chimneys for withdrawal of gas containing aggressive substances
PHKUTT
Type: magnesia spinel
Group: periclase-chrome (MgO ≥ 60%, Cr2O3 4-20%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: heat treated
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for slag belt lining of steel teeming furnaces
SHKU-32
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: lining of steel teeming ladles
SHKU-37
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: lining of steel teeming ladles
SHKU-39
Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: compacted (Ptot 16-20%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: technology
scope of application: lining of steel teeming ladles