PU-7

Type: oxicarbonous
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles

PU-8

Type: oxicarbonous
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles

PU-9

Type: oxicarbonous
Group: periclase-carbonaceous (С 2-40%, MgO ≥ 60%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: for lining of steel teeming ladles

PUBR-90

Type: high-magnesia
Group: periclase (MgO ≥ 85%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: high dense (Ptot 3-10%)
Heat treatment method: unburnt
Molding process: semidry forming
Intended purpose: technology
scope of application: for steel teeming ladle slide gates

SHA

Type: aluminosilicate
Group: chamotte (Al2O3 28-45%)
Refractoriness value: fire resistance (1580 to 1770°С)
Porosity degree: average dense (Ptot 20-30%)
Heat treatment method: burnt
Molding process: semidry forming
Intended purpose: repair/construction
scope of application: products of general purpose for laying of various heat aggregates